Category: Magnets  Publish Time: 2013-08-19 17:20 

Sintered Ferrite Magnets
Ferrite or Ceramic magnets are manufactured from a composite powder containing Iron oxide and Barium or Strontium oxide.

 Sintered Ferrite Magnets

 

Ferrite or Ceramic magnets are manufactured from a composite powder containing Iron oxide and Barium or Strontium oxide. It is most widely used because of its low cost, high-energy, good electric insulation and excellent resistance to demagnetization. The most common type of ceramic magnets are anisotropic strontium, anisotropic barium and isotropic barium magnet.

Ferrites suit a wide range of applications due to their low cost. They are readily available in arc segments, blocks, rings and discs. Principal applications are DC motors, loudspeakers, reed switch operation, magnetic separator assemblies and general holding devices such as pot magnets. The unmagnetized blocks are machined using diamond cutting machines to match customers' exact specification.

Ferrite has an excellent resistance to demagnetization and can be magnetized before or after assembly without danger of losing any performance. It can be used in operating temperatures ranging from -40°C to + 250°C. However it does have a poor temperature coefficient losing approximately 0.2% of remanence per degree C when heated above zero.

There are two manufacturing process for ferrite magnets: Dry Process & Wet Process. By dry process, can produce isotropic & anisotropic magnets; by wet process, only anisotropic magnets can be produced. Isotropic ferrite magnets are not oriented and can be magnetized in any direction; anisotropic ferrite magnets are different, they are all oriented in the manufacturing direction, and should be magnetized in the direction of orientation. For dry process, the tool can be changed and developed easily, while for wet process, it is complicated to change the tool and the tooling charge is much higher.

At present, we have put our emphasis on arc segment magnets for electric DC motors, ring magnets for loudspeakers, disc magnets and block magnets for special applications.

 

Chinese standard - SJ/T 10410 2000 permanent ferrite magnet standard

Material

Br

HcB

HcJ

(BH) max

mT

KG

KA/m

KOe

KA/m

KOe

Kj/m3

MGOe

Y8T

200-235 

2.0-2.35 

125-160 

1.57-2.01 

210-280 

2.64-3.52 

6.5-9.5 

0.8-1.2 

Y20

320-380 

3.2-3.8 

135-190 

1.70-2.38 

140-195 

1.76-2.45 

18.0-22.0 

2.3-2.8 

Y22H

310-360 

3.1-3.6 

220-2500 

2.77-3.14 

280-320 

3.52-4.02 

20.0-24.0 

2.5-3.0 

Y23

320-370 

3.2-3.7 

170-190 

2.14-2.38 

190-230 

2.39-2.89 

20.0-25.5 

2.5-3.2 

Y25

360-400 

3.6-4.0 

135-170 

1.70-2.14 

140-200 

1.76-2.51 

22.5-28.0 

2.8-3.5 

Y26H

360-390 

3.6-3.9

220-250 

2.77-3.14 

225-255 

2.83-3.21 

23.0-28.0 

2.9-3.5 

Y27H

370-400 

3.7-4.0 

205-250 

2.58-3.14 

210-255 

2.64-3.21 

25.0-29.0 

3.1-3.7 

Y28

370-400 

3.7-4.0

175-210 

2.20-2.64 

180-220 

2.26-2.77 

26.0-30.0 

3.3-3.8 

Y30H-1

380-400 

3.8-4.0 

230-275 

2.89-3.46 

235-290 

2.95-3.65 

27.0-32.0 

3.4-4.1 

Y30H-2

395-415 

3.95-4.15 

275-300

3.46-3.77 

310-335 

3.90-4.21 

28.5-32.5 

3.5-4.0 

Y32

400-420

4.0-4.2 

160-190 

2.01-2.38 

165-195 

2.07-2.45 

30.0-33.5 

3.8-4.2

Y33

410-430 

4.1-4.3 

220-250

2.77-3.14 

225-255 

2.83-3.21 

31.5-35.0 

4.0-4.4 

 

MMPA (0100-87) - Permanent ferrite magnet industry standard of USA

Material

Br

HcB

HcJ

(BH) max

mT

KG

KA/m

KOe

KA/m

KOe

Kj/m3

MGOe

C1

 230

2.3

148

1.86

258

3.5

8.36

1.05

C5

 380

3.8

191

2.4

199

2.5

27

3.4

C7

 340

3.4

258

3.23

318

4

21.9

2.75

C8A

  385 

3.85

235

2.95

242

3.05

27.8

3.5

C8B

 420

4.2

232

2.913

236

2.96

32.8

4.12

C9

  380 

3.8

280

3.516

320

4.01

26.4

3.32

C10

 400

4

288

3.617

280

3.51

30.4

3.82

C11

 430

4.3

200

2.512

204

2.56

34.4

4.32

 

 

 

 

Electronic Kiln for sintering ferrite magnets

 